Method for producing fluoropolyether

ABSTRACT

A process for preparing a low-molecular weight fluoropolyether containing an acid fluoride by decomposing a triflate or trifluoroacetate of a fluoropolyether having a hydroxyl group in the presence of a Lewis acid.

TECHNICAL FIELD

The present invention relates to a process for preparing a fluoropolyether by cleavage of a fluoropolyether having a hydroxyl group, the former fluoropolyether being lower than the latter fluoropolyether in molecular weight.

BACKGROUND ART

A fluoropolyether is obtained, for example, by photooxidation of a perfluoroolefin, ring-opening polymerization of a partially fluorinated oxetane compound, fluorination of a hydrogenated polyalkylene compound (Patent Literatures 1 and 2). In these methods, it is generally known that a final product having too much molecular weight is obtained and use thereof is practically restricted. In practice, these high-molecular weight product was applied only to the limited use. Among very interesting applications, there is an application in electric or electronic fields in which a low-molecular weight fluoropolyether is required.

A process is known in which a fluoropolyether having no hydroxyl group is cleaved using a Lewis acid to obtain a low-molecular weight fluoropolyether (Patent Literatures 3).

However, a process is not known in which a fluoropolyether having hydroxyl group is cleaved to obtain a low-molecular weight fluoropolyether, since the fluoropolyether deactivates a Lewis acid.

PATENT LITERATURE

Patent Literature 1: GB 1104482

Patent Literature 2: JP 1985-202122A

Patent Literature 3: U.S. Pat. No. 4,720,527

SUMMARY OF THE INVENTION Problem to be Solved by the Invention

An object of the present invention is to provide a process for preparing a low-molecular weight fluoropolyether containing an acid fluoride by cleavage of a fluoropolyether having a hydroxyl group.

Means for Solving the Problem of the Invention

The present invention provides the following.

1. A process for preparing a low-molecular weight fluoropolyether containing an acid fluoride by decomposing a triflate or trifluoroacetate of a fluoropolyether having a hydroxyl group in the presence of a Lewis acid.

2. A process as defined in claim 1 wherein the triflate is at least one selected among

A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf

TfOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf

A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf

TfOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf

A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf

TfOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf,

A is fluoroalkoxy, Tf is CF₃SO₂, x, y, z and n are a real number of 1 to 100.

3. A process as defined in claim 1 wherein the trifluoroacetate is at least one selected among

A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa

TfaOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa

A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTfa

TfaOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTfa

A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa

TfaOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa,

A is fluoroalkoxy, Tfa is CF₃CO, x, y, z and n are a real number of 1 to 100.

4. A process as defined in claim 1 wherein the acid fluoride is at least one selected among

A-(CF₂CF₂O)xa(CF₂O)ya-CF₂COF

FOC—CF₂O(CF₂CF₂O)xa(CF₂O)ya-CF₂COF

A-(CF₂CF₂CF₂O)za-CF₂CF₂COF

FOC—CF₂CF₂O(CF₂CF₂CF₂O)za-CF₂CF₂COF

A-(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF

FOC—CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF,

A is fluoroalkoxy, 0.1x≤xa≤0.9x, 0.1y≤ya≤0.9y, 0.1z≤za≤0.9z, 0.1n≤na≤0.9n, x, y, z and n are a real number of 1 to 100.

5. A process as defined in any one of claims 2 to 4 wherein x and y are each a real number of 1 to 30, z is a real number of 1 to 30, n is a real number of 1 to 30.

Effect of the Invention

In the present invention, it is possible to prepare a fluoropolyether having a molecular weight lower than a starting fluoropolyether and containing an acid fluoride by modifying a hydroxyl group of the starting fluoropolyether to a triflate or trifluoroacetate and cleaving the fluoropolyether with heating in the presence of a Lewis acid.

EMBODIMENT OF PRACTICING THE INVENTION

Examples of fluoropolyethers having a hydroxyl group are below.

A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OH

HOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OH

A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OH

HOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OH

A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OH

HOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OH,

A is fluoroalkoxy, x, y, z and n are a real number of 1 to 100.

Examples of fluoroalkoxy groups of A are fluoroalkoxy groups having 1 to 6, preferably 2 to 4 and more preferably 2 and 3 carbon atoms. Specific examples are CF₃CF₂CF₂CF₂O, CF₃CF₂CF₂O and CF₃CF₂O.

The above x, y, z and n are each preferably 1 to 70, more preferably 1 to 50 and particularly preferably 1 to 30.

It is possible to prepare a triflate or trifluoroacetate of a fluoropolyether by reacting a trifluoromethanesulfonic anhydride or trifluoroacetic anhydride with a fluoropolyether having a hydroxyl group. The reaction is preferably conducted by using one to three equivalents of trifluoromethanesulfonic anhydride or trifluoroacetic anhydride per equivalent of a hydroxyl group, in the presence of a base, at an atmosphere of an inert gas and at room temperature for 1 to 48 hours with stirring. Examples of bases are pyridine, imidazole and tripropylamine. Examples of inert gas are nitrogen and argon.

Examples of the triflates are

A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf,

TfOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf,

A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf,

TfOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf,

A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf and

TfOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf,

A is fluoroalkoxy, Tf is CF₃SO₂, x, y, z and n are the same as above.

Examples of the trifluoroacetates are

A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa,

TfaOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa,

A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTfa,

TfaOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTfa,

A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa and

TfaOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa,

A is fluoroalkoxy, Tfa is CF₃CO, x, y, z and n are the same as above.

The resulting triflate or trifluoroacetate of the fluoropolyether is decomposed with heating in the presence of a Lewis acid to prepare a low-molecular weight fluoropolyether containing an acid fluoride. Examples of the Lewis acids are a metal oxide such as aluminum oxide, and a metal halide such as aluminum chloride. The reaction is preferably conducted by using 0.1 to 30% by weight of Lewis acid based on the triflate or trifluoroacetate of the fluoropolyether in an atmosphere of an inert gas and at 150 to 350° C. for 1 to 48 hours with heat and stirring.

Examples of the acid fluoride are

A-(CF₂CF₂O)xa(CF₂O)ya-CF₂COF,

FOC—CF₂O(CF₂CF₂O)xa(CF₂O)ya-CF₂COF,

A-(CF₂CF₂CF₂O)za-CF₂CF₂COF,

FOC—CF₂CF₂O(CF₂CF₂CF₂O)za-CF₂CF₂COF,

A-(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF and

FOC—CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF,

A is fluoroalkoxy, 0.1x≤xa≤0.9x, 0.1y≤ya≤0.9y, 0.1z≤za≤0.9z, 0.1n≤na≤9n, x, y, z and n are the same as above.

Preferable are 0.2x≤xa≤0.8 x, 0.2y≤ya≤0.8y, and 0.2n≤na≤0.8n. More preferable are 0.3x≤xa≤0.6x, 0.3y≤ya≤0.6y, 0.3z≤za≤0.6 z, and 0.3n≤na≤0.6n.

In the present invention, a fluoropolyether having a molecular weight lower than a starting fluoropolyether is obtained other than the acid fluoride. Examples of the fluoropolyether are

A-(CF₂CF₂O)xa(CF₂O)ya-B,

A-(CF₂CF₂CF₂O)za-B and

A-(CF₂CF₂CF₂CF₂O)na-B,

A is fluoroalkoxy, B is fluoroalkyl, xa, ya, za and na are the same as above.

Examples of the fluoroalkoxy A are as above and those having 1 to 6, preferably 2 to 4 and further preferably 2 and 3 carbon atoms. Specific examples are CF₃CF₂CF₂CF₂O, CF₃CF₂CF₂O and CF₃CF₂O.

Examples of the fluoroalkyl B are those having 1 to 6, preferably 2 to 4 and further preferably 2 and 3 carbon atoms. Specific examples are —CF₂CF₂CF₂CF₃, —CF₂CF₂CF₃ and —CF₂CF₃.

By reacting a reducing agent such as NaBH₄ or LiAlH₄ with the low-molecular weight fluoropolyether containing an acid fluoride of the present invention (hereinafter referred to as “the present compound), the acid fluoride is modified to a hydroxyl compound. Further, this hydroxyl compound can be converted to a phosphazene compound such as Patent Literature 4 or a compound containing an aromatic ring such as Patent Literature 5.

Patent Literature 4: US 2010/136371A

Patent Literature 5: JP 2009270093A

The above hydroxyl compound derived from the acid fluoride, the phosphazene compound such as Patent Literature 4 or the compound containing an aromatic ring such as Patent Literature 5 (hereinafter referred to as “the compound derived from the present compound) can be used for example as a lubricant for a magnetic disk.

The compound derived from the present compound is applied to the magnetic disk surface preferably by diluting the compound with a solvent and coating the disk surface with the diluted compound. Examples of useful solvents are PF-5060, PF-5080, HFE-7100 and HFE-7200 manufactured by 3M, Vertrel-XF, product of DuPont, etc.

While the compound derived from the present compound is usable singly, the compound can be used also as mixed in a desired ratio with another material, such as Fomblin Zdol, Ztetraol, Zdol TX, AM manufactured by Solvay Solexis, Demnum manufactured by Daikin Industries, Ltd., Krytox manufactured by DuPont, or the like.

Examples of the hydroxyl compound derived from the acid fluoride are

A-(CF₂CF₂O)xa(CF₂O)ya-CF₂CH₂OH,

HO—CH₂CF₂O(CF₂CF₂O)xa(CF₂O)ya-CF₂CH₂OH,

A-(CF₂CF₂CF₂O)za-CF₂CF₂CH₂OH,

HO—CH₂CF₂CF₂O(CF₂CF₂CF₂O)za-CF₂CF₂CH₂OH,

A-(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂CH₂OH and

HO—CH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂CH₂OH,

A is fluoroalkoxy, 0.1x≤xa≤0.9x, 0.1y≤ya≤0.9y, 0.1z≤za≤0.9z, 0.1n≤na≤0.9n, x, y, z and n are the same as above.

The phosphazene compound of Patent Literature 4 is shown by the formula below D-(CH₂—Rf—CH₂O-E-O)n-CH₂—Rf—CH₂-D wherein n is an integer of 1 to 4, D is a group of the formula (a), E is a group of the formula (b), p is 1 or 2, R is fluoroalkyl having 1 to 4 carbon atoms, Rf is —CF₂O(CF₂CF₂O) x′ (CF₂O)y′ CF₂— or —CF₂CF₂O(CF₂CF₂CF₂O)z′ CF₂CF₂—, x′, y′ and z′ are each a real number of 0 to 50.

The compound containing an aromatic ring of Patent Literature 5 is shown by the formula below [HO—(CH₂—R²—CH₂O-G-O)_(n)—CH₂—R²—CH₂—O—CH₂]_(p)—R¹ wherein n is an integer of 0 to 6, G is a group of the formula —CH₂CH(OH) CH₂—, R¹ is an aromatic group of C₆H_(6-p), C₆H_(5-q)—O—C₆H_(5-r) or C₁₀H_(8-p), p is an integer of 3 to 6, q and r are each an integer of at least 0, p=q+r, R² is —CF₂O(CF₂CF₂O)_(x″)(CF₂O)_(y″)CF₂— or —CF₂CF₂O(CF₂CF₂CF₂O)_(z″)CF₂CF₂—, x″ and y″ are each a real number of 0 to 30, z″ is a real number of 1 to 30.

EXAMPLES

The invention will be described in more detail with reference to the following examples to which, however, the invention is not limited.

Example 1

Preparation of A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf (Compound 1) A=CF₃CF₂CF₂O—, Tf=CF₃SO₂—

In an argon atmosphere, 100 g of trifluoromethane-sulfonic anhydride was added dropwise for one hour to a mixture of 570 g of dichloromethane, 285 g of a fluoropolyether of the formula CF₃CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OH (2004 in number average molecular weight and 1.25 in molecular weight distribution) and 34 g of pyridine. The mixture was stirred at room temperature for 17 hours. The mixture was thereafter washed with water, dewatered and purified by silica gel column chromatography, affording 282 g of Compound 1.

Compound 1 was a colorless transparent liquid and 1.74 g/cm³ in density at 20° C. Compound 1 was identified by NMR with the result shown. Compound 1 was 2158 in number average molecular weight which was obtained by a method for determining terminal group using ¹⁹F-NMR (same as hereinafter).

¹⁹F-NMR (solvent: none, reference material: OCF₂CF₂ CF₂O in the obtained product being taken as −129.7 ppm)

δ=−129.7 ppm

[20F, —OCF₂CF₂ CF₂O—]

δ=−83.7 ppm

[40F, —OCF₂ CF₂CF₂ O—]

δ=−124.7 ppm

[2F, —OCF₂ CF₂CH₂OSO₂CF₃]

δ=−86.8 ppm

[2F, —OCF₂CF₂ CH₂OSO₂CF₃]

δ=−76.0 ppm

[3F, —OCF₂CF₂CH₂OSO₂CF₃ ]

δ=−130.7 ppm

[2F, CF₃CF₂ CF₂O—]

δ=−84.7 ppm

[2F, CF₃CF₂CF₂ O—]

δ=−82.4 ppm

[3F, CF₃CF₂CF₂O—]

z=10.2

¹H-NMR (solvent: none, reference material: D₂O)

δ=3.2 ppm

[2H, —OCF₂CF₂CH₂ OSO₂CF₃]

Example 2

Preparation of a mixture (Mixture 1) of CF₃CF₂O(CF₂CF₂CF₂O)_(za)CF₂CF₂COF (Compound 2), FOCCF₂CF₂O(CF₂CF₂CF₂O)_(za)CF₂CF₂COF (Compound 3) and CF₃CF₂CF₂O(CF₂CF₂CF₂O)_(za)CF₂CF₂CF₃ (Compound 4)

In an argon atmosphere, 57 g of Compound 1 (2158 in number average molecular weight and 1.23 in molecular weight distribution) and 3 g of aluminum chloride were heated for reflux at 250° C. for 2 hours. After cooled to room temperature, solid reaction byproducts were filtered off to obtain 28 g of Mixture 1 of Compound 2, Compound 3 and Compound 4 as a filtrate.

Mixture 1 was a light yellow transparent liquid and 1.69 g/cm³ in density at 20° C. Mixture 1 was identified by NMR with the result shown. Mixture 1 was 1045 in number average molecular weight.

¹⁹F-NMR (solvent: none, reference material: OCF₂CF₂CF₂ O in the obtained product being taken as −129.7 ppm)

δ=−129.7 ppm

[9F, —OCF₂CF₂ CF₂O—]

δ=−83.7 ppm

[17F, —OCF₂CF₂ CF₂ O—]

δ=−86.3 ppm

[2F, —OCF₂ CF₃COF]

δ=−122.1 ppm

[2F, —OCF₃CF₂ COF]

δ=−21.7 ppm

[1F, —OCF₂CF₃COF]

δ=−130.7 ppm

[2F, CF₃CF₂ CF₂O—]

δ=−84.7 ppm

[2F, CF₃CF₂CF₂ O—]

δ=−82.4 ppm

[3F, CF₃ CF₂CF₂O—]

za=4.28

Example 3

Preparation of TfaOCH₂CF₂O(CF₂CF₂O)_(x)(CF₂O)_(y)CF₂CH₂OTfa (Compound 5)

Tfa=CF₃CO—

In an argon atmosphere, 50 g of trifluoroacetic anhydride was added dropwise for one hour to 200 g of a fluoropolyether of the formula HOCH₂CF₂O(CF₂CF₂O)x(CF₂O)_(y)CF₂CH₂OH (2071 in number average molecular weight and 1.15 in molecular weight distribution). The mixture was stirred at room temperature for 17 hours. Thereafter, low-boiling components were removed by an evaporator, affording 202 g of Compound 5.

Compound 5 was a colorless transparent liquid and 1.69 g/cm³ in density at 20° C. Compound 5 was identified by NMR with the result shown. Compound 5 was 2265 in number average molecular weight.

¹⁹F-NMR (solvent: none, reference material: OCF₂CF₂ CF₂ CF₂O in the obtained product being taken as −125.8 ppm)

δ=−52.1 ppm, −53.7 ppm, −55.4 ppm

[21F, —OCF₂ O—]

δ=−78.7 ppm, −80.6 ppm

[4F, —CF₂ CH₂OCOCF₃]

δ=−76.7 ppm

[6F, —CF₂CH₂OCOCF₃ ]

δ=−89.1 ppm, −90.7 ppm

[40F, —OCF₂ CF₂ O—]

x=10.1, y=10.4

¹H-NMR (solvent: none, reference material: D₂O)

δ=5.0 ppm

[4H, —OCF₂CH₂ OCOCF₃]

Example 4

Preparation of a mixture (Mixture 2) of CF₃CF₂O(CF₂CF₂O)_(xa) (CF₂O)_(ya)CF₂CF₂COF (Compound 6), FOCCF₂O(CF₂CF₂O)_(xa) (CF₂O)_(ya)CF₂COF (Compound 7) and CF₃CF₂O(CF₂CF₂O)_(xa) (CF₂O)_(ya)CF₂CF₃ (Compound 8)

In an argon atmosphere, 60 g of Compound 5 (2265 in number average molecular weight and 1.14 in molecular weight distribution) and 6 g of aluminum oxide were heated for reflux at 250° C. for 2 hours. After cooled to room temperature, solid reaction byproducts were filtered off to obtain 30 g of Mixture 2 of Compound 6, Compound 7 and Compound 8 as a filtrate.

Mixture 2 was a light yellow transparent liquid and 1.70 g/cm³ in density at 20° C. Mixture 2 was identified by NMR with the result shown. Mixture 2 was 968 in number average molecular weight.

¹⁹F-NMR (solvent: none, reference material: OCF₂CF₂CF₂O in the obtained product being taken as −125.8 ppm)

δ=−52.1 ppm, −53.7 ppm, −55.4 ppm

[8F, —OCF₂ O—]

δ=−78.7 ppm, −80.6 ppm

[4F, —CF₂ CH₂OCOCF₃]

δ=−76.7 ppm

[6F, —CF₂CH₂OCOCF₃ ]

δ=−89.1 ppm, −90.7 ppm

[16.4F, —OCF₂ CF₂ O—]

za=4.10, ya=4.18

Reference Example 1

Preparation of a mixture (Mixture 3) of CF₃CF₂O(CF₂CF₂CF₂O)_(za)CF₂CF₂CH₂OH (Compound 9), HOCH₂CF₂CF₂O(CF₂CF₂CF₂O)_(za)CF₂CF₂CH₂OH (Compound 10) and CF₃CF₂CF₂O(CF₂CF₂CF₂O)_(za)CF₂CF₂CF₃ (Compound 11)

In an argon atmosphere, 10 ml of dehydrated THF is mixed with 0.6 g of LiAlH₄ and ice-cooled. To a mixture was added dropwise a solution of 3 g of Mixture 1 (1045 in number average molecular weight) obtained in Example 2 dissolved in HFE-7100. After the addition, the mixture was stirred for one night at room temperature. To the mixture was added methanol and excess of LiAlH₄ was deactivated, then washed with acid and washed with water. The mixture was dried over dehydrating agent, and the agent was filtered off. The filtrate was concentrated to give 2.4 g of Mixture 3 containing Compound 9, Compound 10 and Compound 11.

Mixture 3 was a light yellow transparent liquid and 1.65 g/cm³ in density at 20° C. Mixture 3 was identified by NMR with the result shown. Mixture 3 was 981 in number average molecular weight. ¹⁹F-NMR (solvent: none, reference material: OCF₂CF₂CF₂O in the obtained product being taken as −129.7 ppm)

δ=−129.7 ppm

[8F, —OCF₂CF₂ CF₂O—]

δ=−83.7 ppm

[16F, —OCF₂ CF₂CF₂ O—]

δ=−86.4 ppm

[2F, —OCF₂ CF₂CH₂OH]

δ=−127.5 ppm

[2F, —OCF₂CF₂ CH₂OH]

δ=−130.7 ppm

[2F, CF₃CF₂ CF₂O—]

δ=−84.7 ppm

[2F, CF₃CF₂CF₂ O—]

δ=−82.4 ppm

[3F, CF₃ CF₂CF₂O—]

za=4.01

¹H-NMR (solvent: none, reference material: D₂O)

δ=4.0 ppm

[2H, —OCF₂CF₂CH₂ OH]

δ=4.3 ppm

[1H, —OCF₂CF₂CH₂OH]

INDUSTRIAL APPLICABILITY

In the present invention, it is possible to prepare a fluoropolyether having a molecular weight lower than a starting fluoropolyether and containing an acid fluoride by modifying a hydroxyl group of the starting fluoropolyether to a triflate or trifluoroacetate and cleaving the fluoropolyether with heating in the presence of a Lewis acid. 

The invention claimed is:
 1. A process for preparing a low-molecular weight fluoropolyether containing an acid fluoride by decomposing a triflate or trifluoroacetate of a fluoropolyether having a hydroxyl group in the presence of a Lewis acid.
 2. The process as defined in claim 1, wherein the fluoropolyether having a hydroxyl group is one having a recurring unit of —(CF₂CF₂O)x(CF₂O)y-, and x and y are a real number of 1 to
 100. 3. The process as defined in claim 1, wherein the fluoropolyether having a hydroxyl group is one having a recurring unit of —(CF₂CF₂CF₂O)z-, and z is a real number of 1 to
 100. 4. The process as defined in claim 1, wherein the fluoropolyether having a hydroxyl group is one having a recurring unit of —(CF₂CF₂CF₂CF₂O)n-, and n is a real number of 1 to
 100. 5. The process as defined in claim 1, wherein the triflate is at least one selected from the group consisting of A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf, TfOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf, A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf, TfOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf, A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf, and TfOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf, wherein A is fluoroalkoxy, Tf is CF₃SO₂, and x, y, z and n are a real number of 1 to
 100. 6. The process as defined in claim 1, wherein the trifluoroacetate is at least one selected from the group consisting of A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa, TfaOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa, A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTfa, TfaOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTfa, A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa, and TfaOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa, wherein A is fluoroalkoxy, Tfa is CF₃CO, and x, y, z and n are a real number of 1 to
 100. 7. The process as defined in claim 1, wherein the acid fluoride is at least one selected from the group consisting of A-(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, FOC—CF₂O(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, A-(CF₂CF₂CF₂O)za-CF₂CF₂COF, FOC—CF₂CF₂O(CF₂CF₂CF₂O)za-CF₂CF₂COF, A-(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, and FOC—CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, wherein A is fluoroalkoxy, 0.1x≤xa≤0.9x, 0.1y≤ya≤0.9y, 0.1z≤za≤0.9z, 0.1n≤na≤0.9n, and x, y, z and n are a real number of 1 to
 100. 8. The process as defined in claim 2, wherein x and y are each a real number of 1 to 30, z is a real number of 1 to 30, and n is a real number of 1 to
 30. 9. The process as defined in claim 1, wherein the acid fluoride is at least one selected from the group consisting of A-(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, FOC—CF₂O(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, A-(CF₂CF₂CF₂O)za-CF₂CF₂COF, FOC—CF₂CF₂O(CF₂CF₂CF₂O)za-CF₂CF₂COF, A-(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, and FOC—CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, and the low-molecular weight fluoropolyether is at least one selected from the group consisting of A-(CF₂CF₂O)xa(CF₂O)ya-B, A-(CF₂CF₂CF₂O)za-B, and A-(CF₂CF₂CF₂CF₂O)na-B, wherein A is fluoroalkoxy, B is fluoroalkyl, 0.1x≤xa≤0.9x, 0.1y≤ya≤0.9y, 0.1z≤za≤0.9z, and 0.1n≤na≤0.9n.
 10. The process as defined in claim 1, wherein the triflate is at least one selected from the group consisting of A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf, TfOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTf, A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf, TfOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf, A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf, and TfOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTf, the acid fluoride is at least one selected from the group consisting of A-(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, FOC—CF₂O(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, A-(CF₂CF₂CF₂O)za-CF₂CF₂COF, FOC—CF₂CF₂O(CF₂CF₂CF₂O)za-CF₂CF₂COF, A-(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, and FOC—CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, and the low-molecular weight fluoropolyether is at least one selected from the group consisting of A-(CF₂CF₂O)xa(CF₂O)ya-B, A-(CF₂CF₂CF₂O)za-B, and A-(CF₂CF₂CF₂CF₂O)na-B, wherein A is fluoroalkoxy, B is fluoroalkyl, Tf is CF₃SO₂, x, y, z and n are a real number of 1 to 100, 0.1x≤xa≤0.9x, 0.1y≤ya≤0.9y, 0.1z≤za≤0.9z, and 0.1n≤na≤0.9n.
 11. The process as defined in claim 1, wherein the trifluoroacetate is at least one selected from the group consisting of A-(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa, TfaOCH₂CF₂O(CF₂CF₂O)x(CF₂O)yCF₂CH₂OTfa, A-(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTf, TfaOCH₂CF₂CF₂O(CF₂CF₂CF₂O)zCF₂CF₂CH₂OTfa, A-(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa, and TfaOCH₂CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)nCF₂CF₂CF₂CH₂OTfa, the acid fluoride is at least one selected from the group consisting of A-(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, FOC—CF₂O(CF₂CF₂O)xa(CF₂O)ya-CF₂COF, A-(CF₂CF₂CF₂O)za-CF₂CF₂COF, FOC—CF₂CF₂O(CF₂CF₂CF₂O)za-CF₂CF₂COF, A-(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, and FOC—CF₂CF₂CF₂O(CF₂CF₂CF₂CF₂O)na-CF₂CF₂CF₂COF, and the low-molecular weight fluoropolyether is at least one selected from the group consisting of A-(CF₂CF₂O)xa(CF₂O)ya-B, A-(CF₂CF₂CF₂O)za-B, and A-(CF₂CF₂CF₂CF₂O)na-B, wherein A is fluoroalkoxy, B is fluoroalkyl, Tfa is CF₃CO, x, y, z and n are a real number of 1 to 100, 0.1x≤xa≤0.9x, 0.1y≤ya≤0.9y, 0.1z≤za≤0.9z, and 0.1n≤na≤0.9n. 